Investigation of the Wear and Hardness Behavior of ST 37 Steel Coated by the Powder Flame Spraying Method

Authors

  • Nurullah Kıratlı Simav Faculty of Technology, Dumlupınar University, Simav, Kütahya, TURKEY

Keywords:

Powder flame spraying, coating, wear.

Abstract

In this study, ST 37 steel was coated with powders of Kobatek 5155, RotoTec®10185 and RotoTec®12486 by using powder flame spraying method. The hardness and wear behavior of coated specimens were investigated.  The wear tests were performed on a pin-on-disc test apparatus. A SiC, 800 sandpaper was used as an abrasive material. The wear tests of coated materials were carried out at room temperature and at the speed of 300 rev/min with 10N loads. Optical microscope investigations were performed to characterize coated specimens. As a result, it was found that each coating powder has the unique effect of improving wear resistance. 

References

[1] Wear behaviour of buldozer rollers welded using a submarget arc welding process, Gülenç, B. and Kahraman, N., Materials Design, 2003; 24, 537-542.
[2] Investigation of the wear behaviour of worn solid railway wheels after filling with different composition of filler metals using MIG-MAG welding methods, Karata?o?lu, F., MSc Thesis, , Gazi Universty, Institute of Science and Technology, 1997.
[3] Metallographic and SEM investigation of the thermally sprayed coatings on steel substrate Iordanova, I., Surtchev, M. and Forcey, K.S., Surf Coat Technol, 2001, 139, 118-126.
[4] Wear behavior of flame-sprayed Al2O3–TiO2 coatings on plain carbon steel substrates, Ku?oglu, I. M., Çelik, E., Çetinel, H., Özdemir, I., Demirkurt, O. and Önel, K., Surface & Coatings Technology, 2005, 200, 1173 – 1177.
[5] An experimental study of the wear performance of NiCrBSi thermal spray coatings, Rodriguez, J., Martin, A., Fernandez, R. and Fernandez, J.E., Wear, 2003; 255, 950–955.
[6] Wear behaviour of thermal flame sprayed FeCr coatings on plain carbon steel substrate Uyulgan, B., Dokumac?, E., Çelik, E., Kayatekin, I., Ak Azem, N.F., Özdemir, I. and Toparli, M.,Journal of Materials Processing Technology, 2007; 190, 204–210.
[7] Alüminyum üzerine uygulanan yüksek karbonlu çelik kaplaman?n a??nma davran???n?n incelenmesi, Kiper, G., Mindivan, H., Samur, R., Kayal?, E. S, ve Çimeno?lu, H., 2004; 10. Denizli Malzeme Sempozyumu ve Sergisi, Denizli, 84-87, 14-16 Nisan.
[8] Ni-Esasl? kaplamalar?n abrazif+erozif a??nma direncine ?s?l püskürtme yönteminin ve WC ilavesinin etkisi, Nejat, Y. S. ve Muharrem, Y., Mühendis ve Makine, 2005; Cilt: 46, Say?: 541, 14-20.
[9] Al-%12Si Malzemesi Üzerine Plazma Püskürtme Tekni?i ile Al-Si+B4C Kaplama, Sar?kaya, Ö., Doktora tezi, Sakarya Üniversitesi Fen Bilimleri Enstitüsü, 2003.
[10] Abrasive wear behaviour of powder flame sprayed coatings on steel substrates, Kahraman, N. and Gülenç, B.,. Materials and Design, 2002; 23, 721–725.
[11] Influence of the deposition techniques on the mechanical properties and microstructure of NiCrBSi coatings, Gomez-del Rio, T., Garrido, M.A., Fernandez, J.E., Cadenas, M. and Rodriguez, J., Journal of materials processing technology, 2008; 204, 304-312.
[12] Protective Si–Al–O–Y glass coatings on stainless steel in situ prepared by combustion flame spraying, Sainz, M.A., Osendi, M.I. and Miranzo, P., Surface & Coatings Technology, 2008; 202, 1712–1717.
[13] Thermal spray coatings of highly reinforced aluminium matrix composites with sol–gel silica coated SiC particles, Torres, B., Campo, M., Urena, A. and Rams, J., Surface & Coatings Technology, 2007; 201, 7552–7559.
[14] Al2O3 kapl? numunelerde kaplama parametrelerinin etkilerinin incelenmesi, Yetgin, S. H. ve Küçükrendeci, ?., 11. Denizli Malzeme Sempozyumu ve Sergisi, Denizli, 2006; 19–21, 359–362.
[15] Wear of Materials, Krause, H. and Beutlar H., The International Conference on Wear of Materials. 1983.
[16] Farkl? tip dolgu elektrodlar? ile dolgular? yap?lan bor k?r?c? çenelerinin a??nma davran??lar?n?n inelenmesi, K?ratl? N., Dumlup?nar üniversitesi, Fen Bilimleri Dergisi, 2006; Say? 12, 117-125.
[17] Application of image analysis for characterization of porosity in thermal spray coatings and correlation with small angle neutron scattering, Deshpande, S., Kulkarni , A., Sampath, S. and Herman, H.,. Surf Coat Technol, 2004; 187, 6–16.
[18] Toz alev püskürtme yöntemi kullan?larak kaplanan alüminyum ala??m?n?n a??nma ve sertlik davran??lar?n?n incelenmesi, K?ratl?, N., Yetgin, S.H. ve Çö?ür, T., Pamukkale Üniversitesi, Mühendislik Bilimleri Dergisi, 2009; Cilt 15, Say? 3, 441-446.

Downloads

Published

2017-05-05

How to Cite

Kıratlı, N. (2017). Investigation of the Wear and Hardness Behavior of ST 37 Steel Coated by the Powder Flame Spraying Method. American Scientific Research Journal for Engineering, Technology, and Sciences, 31(1), 101–108. Retrieved from https://asrjetsjournal.org/index.php/American_Scientific_Journal/article/view/2928

Issue

Section

Articles